T1 - Void swelling of copper and copper alloys induced by heavy ion irradiation
AU - Muroga, Takeo
AU - Matue, Takashi
AU - Watanabe, Hideo
AU - Yoshida, Naoaki
PY - 1999
Y1 - 1999
N2 - Microstructures of Cu, Cu-5Ni and Cu-3.5Zn irradiated with heavy ions at 523 K to 773 K to a dose of 15 dpa were examined. The addition of nickel or zinc was shown to result in an upward shift of the peak void swelling temperature. Although the results are consistent with those of a previous fast neutron irradiation experiment taking difference in the damage rate into account, the microstructural processes seem not to be a simple shift of temperature.
AB - Microstructures of Cu, Cu-5Ni and Cu-3.5Zn irradiated with heavy ions at 523 K to 773 K to a dose of 15 dpa were examined. The addition of nickel or zinc was shown to result in an upward shift of the peak void swelling temperature. Although the results are consistent with those of a previous fast neutron irradiation experiment taking difference in the damage rate into account, the microstructural processes seem not to be a simple shift of temperature.
UR - http://www.scopus.com/inward/record.url?scp=0033323662&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0033323662&partnerID=8YFLogxK
U2 - 10.1520/stp13916s
DO - 10.1520/stp13916s
M3 - Conference article
AN - SCOPUS:0033323662
SN - 1040-3094
SP - 991
EP - 998
JO - ASTM Special Technical Publication
JF - ASTM Special Technical Publication
IS - 1325
T2 - Proceedings of the 1996 18th International Symposium: Effects of Radiation on Materials
Y2 - 25 June 1996 through 27 June 1996
ER -