Ultrathin films of charged polysaccharides assembled alternately with linear polyions

Yuri Lvov, Mitsuhiko Onda, Katsuhiko Ariga, Toyoki Kunitake

研究成果: ジャーナルへの寄稿学術誌査読

137 被引用数 (Scopus)


As a means of preparation of biocompatible molecular surfaces, an alternate assembly of charged polysaccharides and oppositely-charged synthetic polymers was conducted. Cationic chitosan was assembled alternately with anionic poly(sodium styrenesulfonate) (PSS) at pH 4. Regular film growth and its dependence on ionic strength were detected by the quartz crystal microbalance (QCM) method. Averaged film thicknesses for the chitosanCPSS layer were 15, 31, 46, and 69 A°, respectively, when 0, 0.25, 0.5, and 1 M of NaCl was contained in aqueous chitosan. Adsorption of chitosan did not reach saturation in 20 min at 0 M NaCl, while the adsorption became saturated within 6 min with 0.25 M NaCl. Anionic sodium chondroitin sulfate was also assembled in alternation with cationic poly(dimethyldiallylammonium chloride) (PDDA) at pH 6.5. The adsorption of chondroitin sulfate was less sensitive to ionic strength. Surface morphology of chitosan–PSS films was investigated by non-contact atomic force microscopy (AFM) observation. Maximum height difference and Ra value for a 1000 × 1000 nm area were 11 and 0.69 nm, respectively, indicating the formation of a molecularly flat surface by alternate layer-by-layer adsorption.

ジャーナルJournal of Biomaterials Science, Polymer Edition
出版ステータス出版済み - 1月 1 1998

!!!All Science Journal Classification (ASJC) codes

  • 生物理学
  • バイオエンジニアリング
  • 生体材料
  • 生体医工学


「Ultrathin films of charged polysaccharides assembled alternately with linear polyions」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。