Surface characterisation and corrosion behaviour of oxide layer for SLMed-316L stainless steel

W. S.W. Harun, R. I.M. Asri, F. R.M. Romlay, S. Sharif, N. H.M. Jan, F. Tsumori

研究成果: ジャーナルへの寄稿学術誌査読

38 被引用数 (Scopus)

抄録

The stable oxide layer formed through thermal oxidation (TO) process on selective laser melted 316 L stainless steel (SLMed-316 L SS) substrate surface attested to assists in refining their corrosion resistance and observed to behave relatively inert in physiological conditions. The surface characterisation and corrosion behaviour of the oxidised SLMed-316 L SS are the primary focus of this study. The formation of the oxide layer on SLMed-316 L SS was investigated at constant ambient atmosphere and 700 °C temperature for three different soaking times (150, 200 and 250 h). The surface characterisation of the oxide layer was performed using Field Emission Scanning Electron Microscope (FESEM), Energy Dispersive X-ray Spectroscopy (EDX) and X-ray Diffraction (XRD) to correlate the thickness of oxide layer and surface morphology after the TO treatment. Whereas, the electrochemical analysis was conducted using potentiodynamic polarisation to investigate the corrosion behaviour of the oxide layer. The finding disclosed an increase in the oxide layer thickness formation at prolonged exposure in ambient atmosphere. Also, the TO at 150 h showed an improved corrosion behaviour due to the presence of Fe2O3 and Cr2O3 layers. However, the extended soaking time showed no improvement towards the corrosion behaviour.

本文言語英語
ページ(範囲)1044-1052
ページ数9
ジャーナルJournal of Alloys and Compounds
748
DOI
出版ステータス出版済み - 6月 5 2018

!!!All Science Journal Classification (ASJC) codes

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Surface characterisation and corrosion behaviour of oxide layer for SLMed-316L stainless steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル