Self-accomodation and morphology of 14M (7R) martensites in an Ni370at.%Al alloy

Y. Murakami, K. Otsuka, S. Hanada, S. Watanabe

研究成果: ジャーナルへの寄稿学術誌査読

41 被引用数 (Scopus)


The self-accomodation mechanism and morphology of the unique 14M (7R) martensite was studied using single crystals of an Ni370at.%Al alloy. The self-accomodating group was identified by the X-ray diffraction technique, assisted by computer simulations, and it was found that the elastic strains around martensites are effectively cancelled out by making a variant group around the {110&}B2 pole, being similar to other β phase alloys. As a result of extensive observations using a scanning electron microscope and an optical microscope, the basic morphology of the self-accomodating group was found to consist of parallelogram bounded by type I and type II twin bounderies, which is different from the conventional diamond morphology. This basic morphology was supported by the theoretical considerations based on the phenomenological crystallographic theory, and it was shown to be favored over the diamond morphology. Furthermore, the developing mechanism of self-accomodation is proposed, on the basis of the above results.

ジャーナルMaterials Science and Engineering A
出版ステータス出版済み - 12月 20 1994

!!!All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学


「Self-accomodation and morphology of 14M (7R) martensites in an Ni370at.%Al alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。