Relationships between fracture parameters and fracture surface roughness of brittle polymers

K. Arakawa, K. Takahashi

    研究成果: ジャーナルへの寄稿学術誌査読

    105 被引用数 (Scopus)

    抄録

    Fracture parameters such as crack velocity à, stress intensity factor Kd and a specific crack extension resistance R* were measured for Homalite-100, PMMA and epoxy in the course of fast crack propagation using a Cranz-Schardin type high speed camera. Fracture surface roughness λ was evaluated as a function of crack length a so that it could be correlated with the fracture parameters above. The results showed that none of those parameters could be uniquely related to λ. Instead, there was a good correlation between λ and a product R*à.

    本文言語英語
    ページ(範囲)103-114
    ページ数12
    ジャーナルInternational Journal of Fracture
    48
    2
    DOI
    出版ステータス出版済み - 3月 1991

    !!!All Science Journal Classification (ASJC) codes

    • 計算力学
    • モデリングとシミュレーション
    • 材料力学

    フィンガープリント

    「Relationships between fracture parameters and fracture surface roughness of brittle polymers」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル