TY - GEN
T1 - Protectivity and adhesive strength of zinclipscombite coating on 316L stainless steel
AU - Valanezhad, Alireza
AU - Tsuru, Kanji
AU - Maruta, Michito
AU - Matsuya, Shigeki
AU - Ishikawa, Kunio
N1 - Copyright:
Copyright 2020 Elsevier B.V., All rights reserved.
PY - 2013
Y1 - 2013
N2 - Zinclipscombite (ZnFe3+ 2(PO4) 2(OH)2) coating layer was prepared on 316L SS. The 316L SS plates were treated using hydrothermal treatment at 200°C for 2, 6 and 24 h. The ZnFe3+ 2(PO4)2(OH) 2 layer strongly attached to the 316L SS surface. The adhesive strength of the coating layer was measured higher than 65.7 ± 3 MPa. The surface observation and element analysis indicated that the 316L SS plates were covered with ZnFe3+ 2(PO4)2(OH) 2 coating layer after hydrothermal treatment. Linear voltammograms for treated sample at 200°C for 24 h showed higher corrosion resistance. The ICP results proved protective property for the zinclipscombite coating agains PBS solution.
AB - Zinclipscombite (ZnFe3+ 2(PO4) 2(OH)2) coating layer was prepared on 316L SS. The 316L SS plates were treated using hydrothermal treatment at 200°C for 2, 6 and 24 h. The ZnFe3+ 2(PO4)2(OH) 2 layer strongly attached to the 316L SS surface. The adhesive strength of the coating layer was measured higher than 65.7 ± 3 MPa. The surface observation and element analysis indicated that the 316L SS plates were covered with ZnFe3+ 2(PO4)2(OH) 2 coating layer after hydrothermal treatment. Linear voltammograms for treated sample at 200°C for 24 h showed higher corrosion resistance. The ICP results proved protective property for the zinclipscombite coating agains PBS solution.
UR - http://www.scopus.com/inward/record.url?scp=84871291200&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84871291200&partnerID=8YFLogxK
U2 - 10.4028/www.scientific.net/KEM.529-530.251
DO - 10.4028/www.scientific.net/KEM.529-530.251
M3 - Conference contribution
AN - SCOPUS:84871291200
SN - 9783037855171
T3 - Key Engineering Materials
SP - 251
EP - 254
BT - Bioceramics 24
PB - Trans Tech Publications Ltd
T2 - 24th Symposium and Annual Meeting of International Society for Ceramics in Medicine, ISCM 2012
Y2 - 21 October 2012 through 24 October 2012
ER -