Preparation and microstructures of high-current density YBCO films by no-water post-annealing of precursor films including BaF2

Ataru Ichinose, Akihiro Kikuchi, Takanobu Kiss, Kyoji Tachikawa, Shirabe Akita, Kiyoshi Inoue

研究成果: ジャーナルへの寄稿会議記事査読

抄録

Precursor films are deposited on SrTiO3 single crystals at room temperature by the co-evaporation technique using Y, BaF2 and Cu as evaporation sources. Then, the precursor films are annealed in a low-pressure oxygen atmosphere without introduction of water vapor. A sample with a reflection high-energy electron diffraction (RHEED) pattern exhibiting some streaks, Kikuchi lines and Kikuchi zone, which resembles that of a single crystal, is successfully prepared. According to the cross-sectional TEM observation results, epitaxial growth of this YBCO film is achieved for the entire film thickness. The transport properties are measured using a small bridge with a width of 0.1 mm and a length of 1 mm by a standard four-probe method. The obtained YBCO film has a high Jc of over 1 MA/cm 2 at 77 K and a self-field. Furthermore, we discuss the relationship between the epitaxial YBCO layer thickness and the annealing conditions. Approximately 300- and 400-nm-thick epitaxial YBCO films are successfully prepared.

本文言語英語
ページ(範囲)927-931
ページ数5
ジャーナルPhysica C: Superconductivity and its applications
392-396
PART 2
DOI
出版ステータス出版済み - 10月 2003
イベントProceedings of the 15th International Symposium on Superconduc - Yokohama, 日本
継続期間: 11月 11 200211月 13 2002

!!!All Science Journal Classification (ASJC) codes

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • エネルギー工学および電力技術
  • 電子工学および電気工学

フィンガープリント

「Preparation and microstructures of high-current density YBCO films by no-water post-annealing of precursor films including BaF2」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル