Phase transformation and magnetic properties of ferromagnetic Cu-Mn-Ga alloys

Takuro Kushima, Koichi Tsuchiya, Yasukazu Murakami, Daisuke Shindo, Yoshikazu Todaka, Minoru Umemoto

研究成果: ジャーナルへの寄稿学術誌査読

2 被引用数 (Scopus)

抄録

Phase transformation, microstructure and magnetic properties of Cu-(11-14)mol%Mn-20 mol%Ga alloy were investigated. Magnetic domain structures were also investigated by the Lorentz microscopy and electron holography. Plate-like martensite phase (ζ M. ordered hep) was observed in as-quenched Cu-12 mol%Mn-20 mol%Ga. Phase transformation from ζ M martensite to ζ phase (hcp) occurred at around 540 K on heating. The ζ phase decomposed into β (ordered hcp) and β(bcc) phase at around 700 K, then became the single β phase at around 840 K. By subsequent slow cooling, ζ phase was observed at room temperature. Results of the Lorentz microscopy and electron holography revealed that the twin plates of CM martensite and magnetic domains have one-to-one correspondence, suggesting high magneto-crystalline anisotropy energy of the martensite phase. Saturation magnetization and Curie temperature increased with Mn content.

本文言語英語
ページ(範囲)849-855
ページ数7
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
70
10
DOI
出版ステータス出版済み - 10月 2006
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • 凝縮系物理学
  • 材料力学
  • 金属および合金
  • 材料化学

フィンガープリント

「Phase transformation and magnetic properties of ferromagnetic Cu-Mn-Ga alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル