Mode II fatigue crack growth mechanism and threshold in a vacuum and air

Kyohei Toyama, Yoshihiro Fukushima, Yukitaka Murakami

研究成果: ジャーナルへの寄稿学術誌査読

12 被引用数 (Scopus)

抄録

In order to make dear the effect of air on the Mode U fatigue crack growth mechanism and threshold, the Mode II fatigue crack growth test was carried out in a vacuum. Fibrous pattern on the Mode II fatigue fracture surface of the specimen tested in a vacuum was clearer than that tested in air. The side view of the Mode II fatigue crack of the specimen tested in a vacuum was thinner than that tested in air due to the lack of oxidation in a vacuum. The layer with the microstructural change was observed in the vicinity of the Mode II fatigue crack as well as that in air. The Vickers hardness of the layer of the specimen tested in a vacuum was 770 (HV= 630 in air). These values were much higher than that of the original matrix (HV= 190). The layer consisted of very fine grains (∼130nm in a vacuum, ∼100nm in air). The Mode II threshold stress intensity factor ranges, ΔK IIth = 10.2MPa √m (Longitudinal) and 12.5MPa √m (Transverse) in a vacuum were higher than that in air ΔK IIth = 9.4MPa √m (Longitudinal) and 10.8MPa √m (Transverse). Both in a vacuum and air, the values of ΔK IIth for crack growth perpendicular to the rolling direction were higher than the values of ΔK IIth for crack growth parallel to the rolling direction.

本文言語英語
ページ(範囲)719-725
ページ数7
ジャーナルZairyo/Journal of the Society of Materials Science, Japan
55
8
DOI
出版ステータス出版済み - 8月 2006

!!!All Science Journal Classification (ASJC) codes

  • 材料科学一般
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Mode II fatigue crack growth mechanism and threshold in a vacuum and air」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル