Mechanical properties and microstructure of Yb₂SiO₅ environmental barrier coatings under isothermal heat treatment

Yb₂SiO₅ (ytterbium monosilicate) top coatings and Si bond coat layer were deposited by air plasma spray method as a protection layer on SiC substrates for environmental barrier coatings (EBCs) application. The Yb₂SiO₅-coated specimens were subjected to isothermal heat treatment at 1400 °C on air for 0, 1, 10, and 50 h. The Yb₂SiO₅ phase of the top coat layer reacted with Si from the bonding layer and O₂ from atmosphere formed to the Yb₂Si₂O₇ phase upon heat treatment at 1400 °C. The oxygen penetrated into the cracks to form SiO₂ phase of thermally grown oxide (TGO) in the bond coat and the interface of specimens during heat treatment. Horizontal cracks were also observed, due to a mismatch of the coefficient of thermal expansion (CTE) between the top coat and bond coat. The isothermal heat treatment improves the hardness and elastic modulus of Yb₂SiO₅ coatings; however, these properties in the Si bond coat were a little bit decreased.