Low-temperature oriented growth in [CoPt/MgO]n multi-layer

T. Sadoh, M. Kurosawa, M. Kimura, K. Ueda, M. Koyanagi, M. Miyao

研究成果: ジャーナルへの寄稿学術誌査読

抄録

Oriented-crystal growth of CoPt and MgO layers in the [CoPt/MgO]n stacked structures at low-temperatures (< 650 °C) was investigated. For the CoPt (thickness: 40 nm)/MgO (50 nm) structures formed on Si(100) substrates, X-ray diffraction measurements revealed formation of poly-CoPt with random orientations and amorphous MgO. On the other hand, CoPt(111) and MgO(111) layers were dominantly obtained for the [CoPt (4 nm)/MgO (5 nm)]10/Si(100) and [CoPt (2 nm)/MgO (2.5 nm)]20/Si(100) structures. The (111) oriented growth of CoPt layers was found to be due to the template effect of MgO layers, which were crystallized to the (111) orientation if the layers were thin (< 5 nm).

本文言語英語
ページ(範囲)430-433
ページ数4
ジャーナルThin Solid Films
517
1
DOI
出版ステータス出版済み - 11月 3 2008

!!!All Science Journal Classification (ASJC) codes

  • 電子材料、光学材料、および磁性材料
  • 表面および界面
  • 表面、皮膜および薄膜
  • 金属および合金
  • 材料化学

フィンガープリント

「Low-temperature oriented growth in [CoPt/MgO]n multi-layer」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル