Low-cycle fatigue of SUS304 stainless steel under two-step loading (derivation of prefatigue damage-affected small crack growth law and its application to understanding miner's rule)

Y. Fukushima, Sh Harada, Y. Akiniwa, H. Sawada

研究成果: ジャーナルへの寄稿学術誌査読

1 被引用数 (Scopus)

抄録

A small crack growth law-oriented approach was applied to explain the cumulative fatigue damage in a SUS 304 stainless steel which shows cyclic hardening behavior and the effect of prior fatigue damage on the subsequent crack growth rate in the case of two-step strain amplitude. After switching of strain, the stress amplitude and crack growth rate increased or decreased depending on the combination of the first and second strain amplitudes. These changes were interpreted as being induced by the effect of the prefatigue damage or strain history. A modified small crack growth law, compensating the discrepancy between the crack growth rates for constant and two-step strain amplitude, was proposed. Finally the modified crack growth law was found suitable for understanding the Miner rule in the case of materials which exhibit hardening behavior.

本文言語英語
ページ(範囲)1794-1799
ページ数6
ジャーナルNippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
62
600
DOI
出版ステータス出版済み - 1996

!!!All Science Journal Classification (ASJC) codes

  • 材料科学一般
  • 材料力学
  • 機械工学

フィンガープリント

「Low-cycle fatigue of SUS304 stainless steel under two-step loading (derivation of prefatigue damage-affected small crack growth law and its application to understanding miner's rule)」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル