In situ observations of tensile and compressive deformations in semi solid metallic alloys using time-resolved x-ray imaging

Tomoya Nagira, Hideyuki Yasuda, Ryo Unoki, Kouhei Morishita, Akira Sugiyama, Masato Yoshiya, Kentarou Uesugi

研究成果: ジャーナルへの寄稿学術誌査読

5 被引用数 (Scopus)

抄録

Synopsis : Synchrotron X-ray radiography was used to study tensile and compressive deformations of semi solid Al-Cu and/or Fe-C alloys. In the case of tensile deformation of globular Al-Cu sample at ∼60% solid, relatively high strain regions were formed even at mean strain of 0.005. The normal strain rate at the regions was 10 times as high as mean normal strain rate (3.45×10-3s-1). At mean strain of 0.04, tensile deformation was localized in the high strain region, resulting in the formation of internal cracking in the plane normal to the tensile axis. On the other hand, in the case of compressive deformations of globular Al-Cu sample at ∼55 % solid and polygonal Fe-C sample at ∼73% solid, shear bands with decreased solid fraction were formed at the domains tilted by approximately 45 degrees with respect to compressive plane. Rearrangement of solid particles including translation and rotation caused the shear induced dilation at the shear domains. Shear strain was localized at the shear domain with decreased solid fraction. Deformation of the polygonal solid particle of Fe-C sample caused a force to transmit over a longer distance than for the globular Al-Cu sample. Shear fracture finally occurred due to inadequate liquid flow into the expanding spaces between solid particles caused by shear-induced dilation. The solid/solid interaction including impingement between solid particles and rearrangement has significant role in the compressive deformation. These observations demonstrated that the mechanism of cracking formations induced by compressive deformation was totally different from that in the tensile deformation.

本文言語英語
ページ(範囲)668-677
ページ数10
ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
103
12
DOI
出版ステータス出版済み - 2017
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • 凝縮系物理学
  • 物理化学および理論化学
  • 金属および合金
  • 材料化学

フィンガープリント

「In situ observations of tensile and compressive deformations in semi solid metallic alloys using time-resolved x-ray imaging」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル