In situ observation and analysis of faceted crystal growth process in REBCO superconductive oxide

N. Mori; Y. Nakahara; K. Ogi; M. Mukaida

doi:10.1016/j.physc.2007.05.003

In situ observation and analysis of faceted crystal growth process in REBCO superconductive oxide

N. Mori
, Y. Nakahara
, K. Ogi
, M. Mukaida

研究成果: ジャーナルへの寄稿 › 学術誌 › 査読

3 被引用数 (Scopus)

抄録

To clarify the nucleation and growth process of 123 crystals, growth of faceted RE123 (REBa₂Cu₃O_7-X, RE = Nd, Sm, Gd, Y) crystals was observed in situ on MgO(1 0 0) by using high temperature optical microscope with zoom lens. RE123 crystals nucleated and grew at each undercooling (ΔT = 13-50 K). Growth rate (u) and incubation time (t_inc) for nucleation were obtained from the relationship between the position of faceted interface and time (t). u increased with increasing Δ T_r², where ΔT_r = ΔT/T_p, T_p was peritectic temperature. Nucleation rate (I_v) was obtained from the relationship between the number of nucleated crystals (n) and time. I_v increased with increasing of exp (- B / Δ T_r²), where B was a constant. Both u and I_v under a fixed ΔT increased with increasing T_p: u(Nd123) > u(Sm123) > u(Gd123) and I_v(Nd123) > I_v(Sm123) > I_v(Gd123) for T_p(Nd123) > T_p(Sm123) > T_p(Gd123) in Ar-1%O₂ atmosphere.

本文言語	英語
ページ（範囲）	330-334
ページ数	5
ジャーナル	Physica C: Superconductivity and its Applications
巻	463-465
号	SUPPL.
DOI	https://doi.org/10.1016/j.physc.2007.05.003
出版ステータス	出版済み - 10月 1 2007

!!!All Science Journal Classification (ASJC) codes

電子材料、光学材料、および磁性材料
凝縮系物理学
エネルギー工学および電力技術
電子工学および電気工学

文献へのアクセス

10.1016/j.physc.2007.05.003

他のファイルとリンク

引用スタイル

@article{ab53967de3994bcaace1b3dcf4f88186,

title = "In situ observation and analysis of faceted crystal growth process in REBCO superconductive oxide",

abstract = "To clarify the nucleation and growth process of 123 crystals, growth of faceted RE123 (REBa2Cu3O7-X, RE = Nd, Sm, Gd, Y) crystals was observed in situ on MgO(1 0 0) by using high temperature optical microscope with zoom lens. RE123 crystals nucleated and grew at each undercooling (ΔT = 13-50 K). Growth rate (u) and incubation time (tinc) for nucleation were obtained from the relationship between the position of faceted interface and time (t). u increased with increasing Δ Tr2, where ΔTr = ΔT/Tp, Tp was peritectic temperature. Nucleation rate (Iv) was obtained from the relationship between the number of nucleated crystals (n) and time. Iv increased with increasing of exp (- B / Δ Tr2), where B was a constant. Both u and Iv under a fixed ΔT increased with increasing Tp: u(Nd123) > u(Sm123) > u(Gd123) and Iv(Nd123) > Iv(Sm123) > Iv(Gd123) for Tp(Nd123) > Tp(Sm123) > Tp(Gd123) in Ar-1\%O2 atmosphere.",

author = "N. Mori and Y. Nakahara and K. Ogi and M. Mukaida",

year = "2007",

month = oct,

day = "1",

doi = "10.1016/j.physc.2007.05.003",

language = "English",

volume = "463-465",

pages = "330--334",

journal = "Physica C: Superconductivity and its Applications",

issn = "0921-4534",

publisher = "Elsevier B.V.",

number = "SUPPL.",

}

TY - JOUR

T1 - In situ observation and analysis of faceted crystal growth process in REBCO superconductive oxide

AU - Mori, N.

AU - Nakahara, Y.

AU - Ogi, K.

AU - Mukaida, M.

PY - 2007/10/1

Y1 - 2007/10/1

N2 - To clarify the nucleation and growth process of 123 crystals, growth of faceted RE123 (REBa2Cu3O7-X, RE = Nd, Sm, Gd, Y) crystals was observed in situ on MgO(1 0 0) by using high temperature optical microscope with zoom lens. RE123 crystals nucleated and grew at each undercooling (ΔT = 13-50 K). Growth rate (u) and incubation time (tinc) for nucleation were obtained from the relationship between the position of faceted interface and time (t). u increased with increasing Δ Tr2, where ΔTr = ΔT/Tp, Tp was peritectic temperature. Nucleation rate (Iv) was obtained from the relationship between the number of nucleated crystals (n) and time. Iv increased with increasing of exp (- B / Δ Tr2), where B was a constant. Both u and Iv under a fixed ΔT increased with increasing Tp: u(Nd123) > u(Sm123) > u(Gd123) and Iv(Nd123) > Iv(Sm123) > Iv(Gd123) for Tp(Nd123) > Tp(Sm123) > Tp(Gd123) in Ar-1%O2 atmosphere.

AB - To clarify the nucleation and growth process of 123 crystals, growth of faceted RE123 (REBa2Cu3O7-X, RE = Nd, Sm, Gd, Y) crystals was observed in situ on MgO(1 0 0) by using high temperature optical microscope with zoom lens. RE123 crystals nucleated and grew at each undercooling (ΔT = 13-50 K). Growth rate (u) and incubation time (tinc) for nucleation were obtained from the relationship between the position of faceted interface and time (t). u increased with increasing Δ Tr2, where ΔTr = ΔT/Tp, Tp was peritectic temperature. Nucleation rate (Iv) was obtained from the relationship between the number of nucleated crystals (n) and time. Iv increased with increasing of exp (- B / Δ Tr2), where B was a constant. Both u and Iv under a fixed ΔT increased with increasing Tp: u(Nd123) > u(Sm123) > u(Gd123) and Iv(Nd123) > Iv(Sm123) > Iv(Gd123) for Tp(Nd123) > Tp(Sm123) > Tp(Gd123) in Ar-1%O2 atmosphere.

UR - https://www.scopus.com/pages/publications/34548483227

UR - https://www.scopus.com/pages/publications/34548483227#tab=citedBy

U2 - 10.1016/j.physc.2007.05.003

DO - 10.1016/j.physc.2007.05.003

M3 - Article

AN - SCOPUS:34548483227

SN - 0921-4534

VL - 463-465

SP - 330

EP - 334

JO - Physica C: Superconductivity and its Applications

JF - Physica C: Superconductivity and its Applications

IS - SUPPL.

ER -

In situ observation and analysis of faceted crystal growth process in REBCO superconductive oxide

抄録

!!!All Science Journal Classification (ASJC) codes

文献へのアクセス

他のファイルとリンク

フィンガープリント

引用スタイル