Hydrogen embrittlement property of a 1700-MPa-class ultrahigh-strength tempered martensitic steel

Songjie Li, Eiji Akiyama, Kimura Yuuji, Kaneaki Tsuzaki, Nobuyoshi Uno, Boping Zhang

研究成果: ジャーナルへの寄稿学術誌査読

54 被引用数 (Scopus)


The hydrogen embrittlement property of a prototype 1700-MPa-class ultrahigh-strength steel (NIMS17) containing hydrogen traps was evaluated using a slow strain rate test (SSRT) after cathodic hydrogen precharging, cyclic corrosion test (CCT) and atmospheric exposure. The hydrogen content in a fractured specimen was measured after SSRT by thermal desorption spectroscopy (TDS). The relationship between fracture stress and hydrogen content for the hydrogen-precharged specimens showed that the fracture stress of NIMS17 steel was higher, at a given hydrogen content, than that of conventional AISI 4135 steels with tensile strengths of 1300 and 1500 MPa. This suggests better resistance of NIMS17 steel to hydrogen embrittlement. However, hydrogen uptake to NIMS17 steel under CCT and atmospheric exposure decreased the fracture stress. This is because of the stronger hydrogen uptake to the steel containing hydrogen traps than to the AISI 4135 steels. Although NIMS17 steel has a higher strength level than AISI 4135 steel with a tensile strength of 1500 MPa, the decrease in fracture stress is similar between these steels.

ジャーナルScience and Technology of Advanced Materials
出版ステータス出版済み - 2010

!!!All Science Journal Classification (ASJC) codes

  • 材料科学一般


「Hydrogen embrittlement property of a 1700-MPa-class ultrahigh-strength tempered martensitic steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。