Hydrogen embrittlement in a Fe-Mn-C ternary twinning-induced plasticity steel

Motomichi Koyama, Eiji Akiyama, Kaneaki Tsuzaki

研究成果: ジャーナルへの寄稿レター査読

140 被引用数 (Scopus)

抄録

The influence of hydrogen entry on ductility was evaluated in a ternary twinning-induced plasticity (TWIP) steel with a composition of Fe-18Mn-0.6C in wt.% using tensile tests. The samples with a thickness of 1.2. mm were charged with hydrogen galvanostatically during the tensile tests. Significant hydrogen content was introduced by the hydrogen-charging. The total elongation was significantly deteriorated from approx. 60% to 30% by the hydrogen-charging. A clear intergranular fracture surface was observed in a vicinity of the sample surface in the hydrogen-charged samples.

本文言語英語
ページ(範囲)1-4
ページ数4
ジャーナルCorrosion Science
54
1
DOI
出版ステータス出版済み - 1月 2012
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • 化学一般
  • 化学工学一般
  • 材料科学一般

フィンガープリント

「Hydrogen embrittlement in a Fe-Mn-C ternary twinning-induced plasticity steel」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル