T1 - Fracture behavior of Tyranno-ZMI fiber exposed in air at 1173 ∼ 1673 K
AU - Morishita, K.
AU - Hojo, M.
AU - Okuda, H.
AU - Ochiai, S.
AU - Sato, M.
PY - 2005
Y1 - 2005
N2 - The fracture behavior of the Tyranno-ZMI fiber exposed in air at 1173 ∼ 1673K for 2×104s was studied. The average strength of the fiber with SiO2 layer on its surface decreased and the scatter of strength increased with increasing exposure temperature. The fracture of the fiber was controlled by the propagation of the crack made by the premature fracture of the SiO2 layer into fiber. The average strength of the fiber without SiO2 layer prepared by etching away the SiO2 layer from the fiber exposed in air, decreased also with increasing exposure temperature, whereas it was far higher than that of the fiber with SiO 2 layer. The fracture toughness of the fiber, which was originally amorphous decreased with increasing exposure temperature due to the crystallization. In this way, the high temperature-exposure in air caused degradation of the fiber itself and the SiO2 layer-originated crack propagation.
AB - The fracture behavior of the Tyranno-ZMI fiber exposed in air at 1173 ∼ 1673K for 2×104s was studied. The average strength of the fiber with SiO2 layer on its surface decreased and the scatter of strength increased with increasing exposure temperature. The fracture of the fiber was controlled by the propagation of the crack made by the premature fracture of the SiO2 layer into fiber. The average strength of the fiber without SiO2 layer prepared by etching away the SiO2 layer from the fiber exposed in air, decreased also with increasing exposure temperature, whereas it was far higher than that of the fiber with SiO 2 layer. The fracture toughness of the fiber, which was originally amorphous decreased with increasing exposure temperature due to the crystallization. In this way, the high temperature-exposure in air caused degradation of the fiber itself and the SiO2 layer-originated crack propagation.
UR - http://www.scopus.com/inward/record.url?scp=84869826145&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84869826145&partnerID=8YFLogxK
M3 - Conference contribution
AN - SCOPUS:84869826145
SN - 9781617820632
T3 - 11th International Conference on Fracture 2005, ICF11
SP - 788
EP - 793
BT - 11th International Conference on Fracture 2005, ICF11
T2 - 11th International Conference on Fracture 2005, ICF11
Y2 - 20 March 2005 through 25 March 2005
ER -