Fabrication of YBCO film by TFA-MOD process at low-pressure atmosphere

Ryo Teranishi, Tetsuji Honjo, Yoshitaka Tokunaga, Hiroshi Fuji, Junko Matsuda, Teruo Izumi, Akimasa Yajima, Yuh Shiohara

研究成果: ジャーナルへの寄稿学術誌査読

14 被引用数 (Scopus)

抄録

Influence of the process conditions, including the water partial pressure and the total annealing pressure, on YBa2Cu3O 7-y (YBCO) film growth has been investigated in order to increase the growth rate. YBCO films have been fabricated on SrTiO3 substrate by metal-organic deposition using trifluoroacetates (TFA) as a solute source under the low-pressure atmosphere. It was observed that the growth rate of the YBCO film was in proportion to the square root of the water partial pressure and was in inverse proportion to the total pressure. A higher YBCO growth rate was achieved about 3 times as fast as that under the atmospheric fabrication conditions with maintaining the high Jc performance. On the other hand, the volume fraction of a-axis oriented grains in the YBCO film was strongly dependent on the growth rate, a-axis oriented YBCO grains were clearly recognized in the films grown with either very low or very high growth rate. As a result, it was found that the growth region should be controlled to prevent from the growth of the a-axis oriented grains.

本文言語英語
ページ(範囲)920-925
ページ数6
ジャーナルPhysica C: Superconductivity and its applications
412-414
SPEC. ISS.
DOI
出版ステータス出版済み - 10月 2004
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • エネルギー工学および電力技術
  • 電子工学および電気工学

フィンガープリント

「Fabrication of YBCO film by TFA-MOD process at low-pressure atmosphere」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル