Fabrication of vaterite blocks from a calcium hydroxide compact

Kunio Ishikawa, Pery Freitas, Ryo Kishida, Koichiro Hayashi, Akira Tsuchiya

研究成果: ジャーナルへの寄稿学術誌査読

7 被引用数 (Scopus)


Metastable vaterite blocks are expected to show high reactivity. However, they have not been reported to date. In this study, the feasibility of fabricating an artificial vaterite block was investigated by exposing a Ca(OH)2 compact to CO2 under several conditions. Under a 100% H2O atmosphere, a calcite block was formed within three days. Under a 100% methanol atmosphere, no carbonation was observed for seven days. Under 90% methanol without atmospheric flow, a vaterite block containing 5 mass% of unreacted Ca(OH)2 and 3 mass% of calcite was formed after 24 h. On day 7, it was transformed into a block with 70 mass% of calcite, 27 mass% of vaterite, and 3 mass% of unreacted Ca(OH)2. By contrast, under 90% methanol with atmospheric flow to remove the accumulated H2O in the compact, a pure CaCO3 block of 98 mass% vaterite and 2 mass% calcite was formed on day 3. Therefore, the regulation of the amount of H2O is important for fabricating vaterite blocks. Porosimetry measurements revealed that the calcite block fabricated under 90% methanol without atmospheric flow demonstrated a pore size profile closer to that of the vaterite block than that of the calcite block fabricated under 100% H2O atmosphere because the vaterite with small spherical crystals was formed initially before its transformation to calcite.

ジャーナルCeramics International
出版ステータス出版済み - 2月 1 2022

!!!All Science Journal Classification (ASJC) codes

  • 電子材料、光学材料、および磁性材料
  • セラミックおよび複合材料
  • プロセス化学およびプロセス工学
  • 表面、皮膜および薄膜
  • 材料化学


「Fabrication of vaterite blocks from a calcium hydroxide compact」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。