Fabrication of biporous low-crystalline apatite based on mannitol dissolution from apatite cement

Shinye Tajima, Yuji Kishi, Makoto Oda, Michito Maruta, Shigeki Matsuya, Kunio Ishikawa

研究成果: ジャーナルへの寄稿学術誌査読

20 被引用数 (Scopus)

抄録

Biporous (macro- and microporous) calcium phosphate gains much attention as a bone substitute material because of its large surface area and that it improves cell penetration. In the present study, we evaluated the feasibility of biporous, low-crystalline apatite based on dissolution of mannitol from self-setting apatite cement (Biopex®). Mannitol - known as a biocompatible, easily dissolved monosaccharide alcohol - was recrystallized to obtain larger crystals. It was crushed with pestle and mortar, sieved to obtain crystals which passed through a 500-μm mesh but which remained against a 300-μm mesh, and then used as porogen. Although Biopex® containing 60 wt% mannitol was not able to be taken out of the mold, addition of mannitol caused no initial setting inhibition to Biopex® if the amount was 40 wt% or less. Similarly, transformation to apatitic product was confirmed when the apatite cement was immersed in 0.9% saline kept at 37°C for seven days. The set mass became low-crystalline, biporous apatite with approximately 60% porosity.

本文言語英語
ページ(範囲)616-620
ページ数5
ジャーナルdental materials journal
25
3
DOI
出版ステータス出版済み - 2006

!!!All Science Journal Classification (ASJC) codes

  • セラミックおよび複合材料
  • 歯学一般

フィンガープリント

「Fabrication of biporous low-crystalline apatite based on mannitol dissolution from apatite cement」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル