Fabrication and microstructure of Al2O3 matrix composites by in-situ reaction in the Al2O3-La2O3 system

Byung Koog Jang, Teruo Kishi

研究成果: ジャーナルへの寄稿学術誌査読

17 被引用数 (Scopus)

抄録

Al2O3/aluminate composites were fabricated by a solid reaction in the La2O3-Al2O3 system. The formed phase showed elongated morphology that could be controlled by varying the hot-pressing temperature and time. Dense Al2O3/LaAl11O18 composites were fabricated by hot-pressing above 1500°C. When the hot-pressing temperature was 1400°C, Al2O3/LaAlO3 composites were formed from starting composition. The grain size of monolithic alumina ceramics increased with increasing hot-pressing temperature, and marked grain growth occurred above 1600°C. However, the elongated LaAl11O18 phase suppressed the growth of alumina grains in the Al2O3/LaAl11O18 composites. Small LaAl11O18 grains existed in the alumina grains as an intragranular phase, while needlelike grains with a large aspect ratio existed at Al2O3 grain boundaries. The amount of in-situ formed LaAl11O18 phase increased with increasing amount of La2O3, and the aspect ratio of LaAl11O18 grains increased with increasing hot-pressing time.

本文言語英語
ページ(範囲)739-743
ページ数5
ジャーナルJournal of the Ceramic Society of Japan
106
8
DOI
出版ステータス出版済み - 8月 1998
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • セラミックおよび複合材料
  • 化学一般
  • 凝縮系物理学
  • 材料化学

フィンガープリント

「Fabrication and microstructure of Al2O3 matrix composites by in-situ reaction in the Al2O3-La2O3 system」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル