Effect of temperature and CO2 concentration on gasification behavior of carbon fiber containing fine iron particles

Kazuto Nishihiro, Takayuki Maeda, Ko ichiro Ohno, Kazuya Kunitomo

    研究成果: ジャーナルへの寄稿学術誌査読

    1 被引用数 (Scopus)


    In direct reduced iron (DRI) process, CO–H2 gas mixture is used as a reducing agent, which may make the operation unstable owing to a carbon deposition reaction and metal dusting reaction through Fe3C. The Fe3C decomposition reaction forms iron particles which acts as a catalyst for a carbon fiber deposition reaction at around 600°C. Such a carbon fiber deposition not only causes the loss of the carbon but also decrease the reducibility of the gas. On the other hand, the carbon fiber is likely gasified by CO–CO2 gas mixture at around 1 000°C. In the present study, the carbon fiber gasification was quantitative analyzed using thermobalance to clarify the mechanism of the carbon fiber gasification reaction. To prepare a carbon fiber sample, the carbon was deposited with a reduced iron catalyst at 600°C in 50vol%CO-50vol%H2. Carbon fiber containing fine iron particles was gasified with various compositions of CO–CO2 gas mixture at 1 000°C. Further, the effect of temperature of the gasified reaction was also investigated at 800°C, 900°C and 1 000°C in 100vol%CO2. According to XRD analysis of the sample after gasification, Fe3C in the sample before gasification decomposed to iron and a portion of iron was oxidized to Fe3O4 and FeO when gasification ratio was high. The transition of carbon fiber shape was confirmed by SEM observation. Fine iron particles located on the tip of carbon fiber were sintered during gasification of carbon fiber. The mechanism of carbon fiber gasification was evaluated considering crystalline size, such as La and Lc that show (002) and (110) determined by XRD analysis, respectively. It was found that the La decreased with gasification ratio at all temperatures. In addition, Lc decreased after gasification at 1 000°C.

    ジャーナルisij international
    出版ステータス出版済み - 2019

    !!!All Science Journal Classification (ASJC) codes

    • 材料力学
    • 機械工学
    • 金属および合金
    • 材料化学


    「Effect of temperature and CO2 concentration on gasification behavior of carbon fiber containing fine iron particles」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。