Iron carburization is one of the most important reactions in iron making process. Ifthe rate and efficiency of carburization reaction are increased, energy consumption of the process will be reduced to a large extent. The purpose of this study is to clarify the effect of carbon structure on initial iron carburization behavior for suggestion of effective carbon utilization in iron making process. Samples of different carbon structures were prepared by heat treatment of CH4 decomposed carbon at various temperatures. Carbon structures of prepared carbon samples were analyzed by a Raman spectroscopy. Forexperiments, high-purity iron samples directly-contacted with carbon were prepared. A laser microscope combined with an infrared image furnace was used for heating of the sampleand "in-situ" observation of carburization phenomena. Carbon concentration profile in ironsample was analyzed by a wavelength dispersion type electron probe micro analyzer. The results of this work showed that primary Fe-C liquid formation temperature becamelower from 1439 to 1431K with use of lower crystallization carbon. It was indicated that utilization of the lower crystallization degree of carbon structure causes formation of primary Fe-C liquid at the lower temperature.
|ジャーナル||Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan|
|出版ステータス||出版済み - 2010|
!!!All Science Journal Classification (ASJC) codes