Diffusion characteristics in anode-substrates for anode-supported SOFCs

Yoshio Matsuzaki, Yoshitaka Baba, Teruhiro Sakurai

研究成果: ジャーナルへの寄稿学術誌査読

4 被引用数 (Scopus)

抄録

We have operated the single-cells in the stack structure using methane as a fuel under high fuel utilizations. Methane fuel was supplied directly to the cell-stack after addition of steam at a steam to carbon ratio of 2. A steam-reforming reaction was conducted directly on the anode (direct internal reforming: DIR). In the case of the single-cell with the anode-substrate having relatively high porosity, stack voltage was found to be 0.767 V at fuel utilization of 75%, at which d.c. energy conversion efficiency is 50.2%(HHV). A maximum energy conversion efficiency, 53.6%, was achieved at fuel utilization of 86% and cell voltage of 0.712 V. This methane-to-electricity conversion efficiency will be high enough for practical applications. For anode-supported SOFCs, concentration polarization loss in the anode can be a crucial problem because fresh fuel and electrochemical reaction products have to diffuse through a thick anode substrate in the opposite direction between the flow field (fuel distribution channel) and the anode/electrolyte interface. Limiting current density with a diluted CO at a fixed current density was measured and analyzed to investigate the diffusion characteristics of a fuel in the anode-substrates. Diffusion parameters obtained by the analysis were verified by measurement of the limiting current density with diluted H2 and voltage response for depolarization process after current-interruption.

本文言語英語
ページ(範囲)484-488
ページ数5
ジャーナルElectrochemistry
73
7
DOI
出版ステータス出版済み - 7月 2005
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • 電気化学

フィンガープリント

「Diffusion characteristics in anode-substrates for anode-supported SOFCs」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル