Compressive deformation behavior of porous PLLA/PCL polymer blend

Mitsugu Todo, Joo Eon Park, Hiroyuki Kuraoka, Jin Woong Kim, Kentaro Taki, Masahiro Ohshima

    研究成果: ジャーナルへの寄稿学術誌査読

    15 被引用数 (Scopus)

    抄録

    Porous poly(L-lactide)/poly(e-caplolactone) (PLLA/PCL) was fabricated by using the solid-liquid phase separation method and the solvent sublimation process. Pelletized PLLA and PCL with a mixture ratio of 80:20 were dissolved in 1,4-dioxane to prepare PLLA/PCL solution of 7 wt%. The solution was then filled into a PP tube, and frozen from the bottom part at a constant rate in liquid nitrogen to induce solid-liquid phase separation. Cylindrical specimens of 8-mm diameter and 12-mm length were then fabricated. Compression tests of the porous specimens were conducted by using a conventional testing machine, and the compressive mechanical properties such as the critical stress and the modulus were evaluated. It is observed that these mechanical properties of PLLA/PCL stands between pure PLLA and PCL, indicating that the compressive properties of the biodegradable scaffolds can be controlled by using polymer blending.

    本文言語英語
    ページ(範囲)4191-4194
    ページ数4
    ジャーナルJournal of Materials Science
    44
    15
    DOI
    出版ステータス出版済み - 8月 2009

    !!!All Science Journal Classification (ASJC) codes

    • 材料科学一般
    • 材料力学
    • 機械工学

    フィンガープリント

    「Compressive deformation behavior of porous PLLA/PCL polymer blend」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル