Architectural design of cellulose monolayer at au interface

Shingo Yokota, Takuya Kitaoka, Hiroyuki Wariishi

研究成果: ジャーナルへの寄稿会議記事査読


Flat cellulose film surfaces were architecturally designed by spin-coating or self-assembling in the cellulose/N-methylmorpholine-N-oxide/H2O system. Spin-coated cellulose films were allowed to stably separate out onto the silicon oxide wafer pretreated with cationic polymer. Atomic force microscopic (AFM) images of the cellulose surface pretreated with cationic polyvinylamine showed an anisotropic morphology, suggesting the specific interaction at a cellulose/polymer interface. Changing poor solvents provided the variation of the surface roughness, being possibly dependent on the behavior of cellulose precipitation. Cellulose self-assembled monolayer (SAM) was successfully formed on an Au plate with cellulose derivative whose reducing ends were selectively modified with thiosemicarbazide (TSC) in NMMO solution. The cellulose SAM at Au interface possessed a parallel-packed crystalline structure analogous to native cellulose, and a flat surface at sub nano-meter level from the results obtained by electron diffractometry and AFM observation, respectively. It was strongly suggested that the cellulose-TSC molecular chains were regularly arranged on the Au surface through a covalent S-Au bonding. These techniques would provide novel cellulose architectures designed for cellulose-based material science.

ジャーナルAppita Annual Conference
出版ステータス出版済み - 2005
イベント59th Appita Annual Conference and Exhibition, incorporating the 13th ISWFPC: International Symposium on Wood, Fibre and Pulping Chemistry - Auckland, ニュージ―ランド
継続期間: 5月 16 20055月 19 2005

!!!All Science Journal Classification (ASJC) codes

  • メディア記述


「Architectural design of cellulose monolayer at au interface」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。