A new design concept for prevention of hydrogen-induced mechanical degradation: Viewpoints of metastability and high entropy

Motomichi Koyama, Takeshi Eguchi, Kenshiro Ichii, Cemal Cem Tasan, Kaneaki Tsuzaki

研究成果: ジャーナルへの寄稿会議記事査読

7 被引用数 (Scopus)


"How crack growth is prevented" is key to improve both fatigue and monotonic fracture resistances under an influence of hydrogen. Specifically, the key points for the crack growth resistance are hydrogen diffusivity and local ductility. For instance, type 304 austenitic steels show high hydrogen embrittlement susceptibility because of the high hydrogen diffusivity of bcc (α) martensite. In contrast, metastability in specific austenitic steels enables fcc (γ) to hcp (ϵ) martensitic transformation, which decreases hydrogen diffusivity and increases strength simultaneously. As a result, even if hydrogen-assisted cracking occurs during monotonic tensile deformation, the ϵ-martensite acts to arrest micro-damage evolution when the amount of ϵ-martensite is limited. Thus, the formation of ϵ-martensite can decrease hydrogen embrittlement susceptibility in austenitic steels. However, a considerable amount of ϵ-martensite is required when we attempt to have drastic improvements of work hardening capability and strength level with respect to transformation-induced plasticity effect. Since the hcp structure contains a less number of slip systems than fcc and bcc, the less stress accommodation capacity often causes brittle-like failure when the ϵ-martensite fraction is large. Therefore, ductility of ϵ-martensite is another key when we maximize the positive effect of ϵ-martensitic transformation. In fact, ϵ-martensite in a high entropy alloy was recently found to be extraordinary ductile. Consequently, the metastable high entropy alloys showed low fatigue crack growth rates in a hydrogen atmosphere compared with conventional metastable austenitic steels with α-martensitic transformation. We here present effects of metastability to ϵ-phase and configurational entropy on hydrogen-induced mechanical degradation including monotonic tension properties and fatigue crack growth resistance.

ジャーナルProcedia Structural Integrity
出版ステータス出版済み - 2018
イベント22nd European Conference on Fracture, ECF 2018 - Belgrade, セルビア
継続期間: 8月 25 20188月 26 2018

!!!All Science Journal Classification (ASJC) codes

  • 材料力学
  • 機械工学
  • 材料科学一般
  • 土木構造工学


「A new design concept for prevention of hydrogen-induced mechanical degradation: Viewpoints of metastability and high entropy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。