Transformation of Bi,Pb-2223 phase from multilayered precursor films

Akiyoshi Matsumoto, Hitoshi Kitaguchi, Yusuke Shimada, Satoshi Hata

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)


Bi,Pb-2223 phase on SrTiO3(100) fabricated by RF sputtering and annealing method have been investigated. We tried to fabricate Bi,Pb-2223 phase using multilayered precursors of Bi-2212 and Ca-Cu-Pb-O. We fabricated a multilayered film as a precursor by using two kinds of sputtering targets of Bi,Pb-2212 and Ca-Cu-Pb-O. After deposition by sputtering, the multi-layered precursor was annealed with Bi,Pb-2223 pellets at 840 °C for 100 h. From the X-ray diffraction (XRD) measurements, the main peaks of the precursor film were of Bi,Pb-2212 phase, but still remained large impurity phase. From the transmission electron microscopy (TEM) and Scanning Transmission Electron Microscopy (STEM) observation, we confirmed that a multilayer combination of a Bi,Pb-2212 layer and Ca-Cu-Pb-O layer was formed. After annealing, we determined the Tc through resistance measurements. The Tc value determined by the four-probe method was Tczero = 104.K. Furthermore, we observed two phases of Bi,Pb-2223 and Bi,Pb-2212 by XRD measurement. These results suggest that the Bi,Pb-2223 phase transformed from multilayered precursor film of Bi,Pb-2212 and Ca-Cu-Pb-O formed.

Original languageEnglish
Article number8673641
JournalIEEE Transactions on Applied Superconductivity
Issue number5
Publication statusPublished - Aug 2019

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Electrical and Electronic Engineering


Dive into the research topics of 'Transformation of Bi,Pb-2223 phase from multilayered precursor films'. Together they form a unique fingerprint.

Cite this