Tomographic dark-field TEM observation of ordered precipitates in a Ni-Mo alloy

Kosuke Kimura, Takao Horiuchi, Satoshi Hata, Syo Matsumura

Research output: Contribution to specialist publicationArticle

1 Citation (Scopus)


A Ni-Mo alloy treated in a solution was annealed at 1073K for 24 hours to obtain a two-phase nanostructure. It is composed of the nickel matrix with a face-centered cubic (fcc) structure and Ni4Mo precipitates with a D1a body-centered tetragonal superstructure. When Ni4Mo precipitates are formed in the nickel matrix, six types of orientation relationships exist between the precipitates and the matrix. Its etchant was an electrolysis polishing solution with composition CH3OH : HSO4 = 3:1 and mthe magnification of the dark-field image was 26000X.

Original languageEnglish
Number of pages2
Specialist publicationAdvanced Materials and Processes
Publication statusPublished - Feb 2006

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering


Dive into the research topics of 'Tomographic dark-field TEM observation of ordered precipitates in a Ni-Mo alloy'. Together they form a unique fingerprint.

Cite this