Thermal expansion and phase transition behavior of Al2-xM x(WO4)3 (M = Y, Ga and Se) ceramics

Takayuki Sugimoto, Yuhshi Aoki, Eiki Niwa, Takuya Hashimoto, Yuko Morito

Research output: Contribution to journalArticlepeer-review

25 Citations (Scopus)


In order to obtain materials with a tailored thermal expansion, in particular zero-thermal-expansion between - 50-100°C, the possibility of preparation, thermal expansion behavior and phase transition of Al 2-xMx (WO4)3 (M: Y, Ga and Sc) have been examined. Y was not substituted for the Al site in Al2(WO 4)3. Al2-xGax (WO4) 3 single phase could be prepared in x range as high as 0.4. The phase transition temperature involving abrupt expansion increased with an increase of Ga content, resulting in no phase transition for Al1.6Ga 0.4 (WO4)3 between -50-100°C. However, zero-thermal expansion could not be obtained in Al2-xGa x(WO4)3 at the temperature range. Al 2-xScx(WO4)3 single phase was obtained for the whole x range. The temperature of the phase transition decreased with an increase of Sc content and the abrupt expansion due to the phase transition disappeared above - 50°C for the specimen with x larger than 0.3. The thermal expansion coefficient could be controlled with Sc content and zero-thermal-expansion was observed for the specimens with x around 0.1 and 1.5.

Original languageEnglish
Pages (from-to)176-181
Number of pages6
JournalJournal of the Ceramic Society of Japan
Issue number1339
Publication statusPublished - Mar 2007
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • General Chemistry
  • Condensed Matter Physics
  • Materials Chemistry


Dive into the research topics of 'Thermal expansion and phase transition behavior of Al2-xM x(WO4)3 (M = Y, Ga and Se) ceramics'. Together they form a unique fingerprint.

Cite this