The improvement of optical reactivity for TiO2 thin films by N2-H2 plasma surface-treatment

Lei Miao, Sakae Tanemura, Hiroshige Watanabe, Yukimasa Mori, Kenji Kaneko, Shoichi Toh

    Research output: Contribution to journalArticlepeer-review

    103 Citations (Scopus)


    To improve the optical reactivity of TiO2 thin film in visible-light region, sputter-deposited anatase film on slide glass substrate with 1200Å film thickness was surface-treated by N2-H 2 mixed gases plasma and additionally anneal-treated in N 2 gases at 400°C for 2h. The absorption edges of plasma-treated sample and plasma plus anneal-treated one shifted from 363nm (3.4eV) to 428nm (2.9eV), and 354nm (3.5eV) to 428nm (2.9eV), while the absorptance for the two corresponding samples increased by 16% and 26%, respectively, in comparison with the as-deposited sample. Spectral absorption is well explained by Tauc-plot extrapolated band-gap using extinction coefficient k obtained from spectroscopic ellipsometry for the surface layers of the three samples, even though in the case of plasma plus anneal-treated sample showed only nominal band-gap value (2.65eV) due to the metallic behavior of extinction coefficient k in lower energy range (2.5eV). X-ray photoemission spectroscopy reveals the formation of TiO2-xNx and TiN deep into about 120Å thickness from the film surface for both plasma-treated and plasma plus anneal-treated samples. Secondary ion mass spectrography also detected high concentration of N element at the surface of the two corresponding samples. From the fact of formation of TiN and TiO2-xNx, N-doping in this work was proved as N substituted O in TiO2 lattice. We confirmed this substitutional N-doping causes the narrowing of band-gap that resulted in the observed significant red shift of the absorption edge to the visible-light region.

    Original languageEnglish
    Pages (from-to)118-124
    Number of pages7
    JournalJournal of Crystal Growth
    Issue number1-2
    Publication statusPublished - Jan 2 2004

    All Science Journal Classification (ASJC) codes

    • Condensed Matter Physics
    • Inorganic Chemistry
    • Materials Chemistry


    Dive into the research topics of 'The improvement of optical reactivity for TiO2 thin films by N2-H2 plasma surface-treatment'. Together they form a unique fingerprint.

    Cite this