The electrochemical properties of Fe2O3-loaded carbon electrodes for iron-air battery anodes

Bui Thi Hang, Tomonori Watanabe, Minato Eashira, Shigeto Okada, Jun Ichi Yamaki, Satoshi Hata, Seong Ho Yoon, Isao Mochida

Research output: Contribution to journalArticlepeer-review

64 Citations (Scopus)


The redox efficiency of iron has been improved by increasing the distribution of iron on the carbon surface with Fe2O 3-loaded carbon materials. The Fe2O3-loaded carbon material was prepared by loading Fe2O3 on carbon by a chemical method. Fe(NO3)3 was impregnated on carbon with different weight ratios of iron-to-carbon in an aqueous solution, and the mixture was dried and then calcined for 1 h at 400 °C in flowing Ar. The effect of various carbons on the physical and electrochemical properties of Fe2O3-loaded carbon electrodes was investigated with the use of X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM) along with X-ray energy-dispersive spectroscopy (EDS), cyclic voltammetry (CV) and galvanostatic cycling performance. Transmission electron microscopy coupled with X-ray diffraction measurements revealed that small Fe2O3 particles were distributed on the carbon surface. Natural graphite and several nano-carbon materials such as acetylene black and tubular carbon nanofibers (tubular CNF) exhibited improved characteristics, such as enhanced capacity and higher redox currents for the Fe2O3-loaded carbon electrode. SEM and EDS results suggest that Fe2O3-loaded nano-carbon electrodes, due to the large surface area of the nano-carbon, have more Fe2O3 dispersed than on Fe2O3-coated graphite electrodes.

Original languageEnglish
Pages (from-to)261-271
Number of pages11
JournalJournal of Power Sources
Issue number1-2
Publication statusPublished - Oct 4 2005

All Science Journal Classification (ASJC) codes

  • Renewable Energy, Sustainability and the Environment
  • Energy Engineering and Power Technology
  • Physical and Theoretical Chemistry
  • Electrical and Electronic Engineering


Dive into the research topics of 'The electrochemical properties of Fe2O3-loaded carbon electrodes for iron-air battery anodes'. Together they form a unique fingerprint.

Cite this