The effect of interacting small defects on the fatigue limit of a medium carbon steel

Mari Åman, Saburo Okazaki, Hisao Matsunaga, Gary B. Marquis, Heikki Remes

Research output: Contribution to journalArticlepeer-review

4 Citations (Scopus)


Structural steels contain various material irregularities and natural defects. These cause local stress concentrations, from which fatigue cracks tend to initiate. Two defects in close proximity to each other may affect local stress distributions and thus, begin to interact. In this paper, the effect of interacting small cracks on the fatigue limit is systematically investigated in a medium carbon steel. The growth of interacting cracks, as well as the characteristics of non-propagating cracks and microstructural aspects were closely examined via the plastic replica method. It was found that although the fatigue limit is essentially controlled by the mechanics of interacting cracks, based on their configuration, the local microstructure comprised of ferrite and pearlite has a statistical scatter effect on the behaviour of interacting cracks and non-propagating thresholds. With respect to the fatigue limit, when two defects were in close proximity, they behaved as would a larger single defect. However, with greater spacing between defects, rather than mechanical factors, it is the local microstructure which determines the location and characteristics of non-propagating cracks.

Original languageEnglish
Pages (from-to)3322-3329
Number of pages8
JournalProcedia Structural Integrity
Publication statusPublished - 2016

All Science Journal Classification (ASJC) codes

  • Mechanical Engineering
  • Mechanics of Materials
  • Civil and Structural Engineering
  • General Materials Science


Dive into the research topics of 'The effect of interacting small defects on the fatigue limit of a medium carbon steel'. Together they form a unique fingerprint.

Cite this