Structure and polarization properties of Zn-Nb films formed on steel sheet by sputtering

Hiroshi Kuboyama, Hiroaki Nakano, Satoshi Oue, Hisaaki Fukushima, Masataka Masuda, Shunichi Hashimoto

    Research output: Contribution to journalArticlepeer-review


    Zn-Nb films were formed on a steel sheet by helicon plasma sputtering in an argon gas atmosphere at 1.0 Pa, at RF power of 50 W and DC power of 50 mA. The structure and polarization properties of these films were studied using EPMA, X-ray diffraction and polarization curve measurements. Zn plate-like crystals in Zn-Nb films decreased with increasing Nb content, resulting in a smooth surface over the entire film at Nb content of 30 mass% and above. The preferred orientation plane of Zn plate-like crystals was (0002) at 0 mass% Nb, while the orientation indices of (101̄1) and (101̄0)Zn increased with rising Nb content. At 30-60 mass% Nb, the X-ray diffraction spectra showed a halo pattern characteristic of an amorphous structure. The corrosion current of Zn-Nb films, which was determined by polarization curves in 3% NaCl solution, decreased with increasing Nb content to reach a minimum value at 30-60 mass% Nb, corresponding to an amorphous structure.

    Original languageEnglish
    Pages (from-to)1205-1209
    Number of pages5
    Journalisij international
    Issue number8
    Publication statusPublished - 2006

    All Science Journal Classification (ASJC) codes

    • Mechanics of Materials
    • Mechanical Engineering
    • Metals and Alloys
    • Materials Chemistry


    Dive into the research topics of 'Structure and polarization properties of Zn-Nb films formed on steel sheet by sputtering'. Together they form a unique fingerprint.

    Cite this