Radiation effects in ferrate garnet

S. Utsunomiya, S. Yudintsev, R. C. Ewing

Research output: Contribution to journalArticlepeer-review

41 Citations (Scopus)


Radiation effects in four synthetic ferrate garnets (A3B 2(XO4)3, Ia3d, Z = 8) were examined by ion beam irradiations with in situ observation (T = 298-873 K) using transmission electron microscopy (TEM) at the IVEM Tandem Facility at Argonne National Laboratory. The garnet compositions include: A = Ca, Gd, Th, and Ce; B = Zr, Fe. The critical amorphization temperatures (Tc), the temperature above which the target material cannot be amorphized due to dynamic annealing, were between 820 and 870 K. The amorphization doses at room temperature are between 0.17 and 0.19 dpa (displacement per atom), which is similar to that of silicate- and aluminate-garnets. The small variations in the amorphization dose and Tc of the different compositions suggest that radiation effects in ferrate garnets are structurally constrained. Qualitative analyses of the valence states of Ce and Fe in garnet before and after irradiation were completed using electron energy-loss spectroscopy (EELS). The Ce and Fe in the unirradiated garnet were dominantly trivalent and divalent, respectively. The characteristic peaks of Ce4+, at ∼5 eV higher energy for the M-edges, were present in unirradiated garnet as a minor peak, and the peaks did not disappear after complete amorphization, suggesting that the valence state did not change significantly. EELS analysis was conducted on a nearly pure andradite, Ca3Fe2Si3O12, which ideally contains only ferric iron. The andradite was amorphized at 0.18 dpa. EELS analysis revealed that some of ferric iron was converted to ferrous iron during the irradiation.

Original languageEnglish
Pages (from-to)251-260
Number of pages10
JournalJournal of Nuclear Materials
Issue number2-3
Publication statusPublished - Feb 1 2005
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • Nuclear and High Energy Physics
  • General Materials Science
  • Nuclear Energy and Engineering


Dive into the research topics of 'Radiation effects in ferrate garnet'. Together they form a unique fingerprint.

Cite this