Paper-structured catalyst containing CeO2–Ni flowers for dry reforming of methane

Phuc Hoan Tu, Diep Ngoc Le, Trung Dung Dao, Quang Tuyen Tran, Tin Chanh Duc Doan, Yusuke Shiratori, Chien Mau Dang

Research output: Contribution to journalArticlepeer-review

27 Citations (Scopus)


In this paper, ceria flowers containing nano-sized catalyst Ni particles were prepared on alumina-silica fiber network for production of hydrogen from biogas. The CeO2 flowers were prepared using hydrothermal method and then NiO was loaded on the CeO2 flowers by impregnation method. The Paper-structured catalysts (PSCs) were prepared from alumina-silica fibers and the CeO2–NiO flowers using conventional paper making method. The loaded NiO particles were uniformly dispersed on the CeO2 flowers with the use of polyvinylpyrrolidone as a dispersion enhancer, which was observed by FE-SEM and EDX analysis. The NiO particles were then reduced into Ni by using H2. The PSCs containing CeO2–Ni flowers with various Ni contents (2.1, 3.4, and 4.6%) were used for dry reforming of CH4. It was found that 3.4% amount of Ni on the PSC was suitable for reforming reaction, and the higher amount of Ni (4.6%) did not increase the CH4 conversion. The PSC with the CeO2 flowers had porous structure and large surface area leading to the better dispersion of the Ni particles with smaller size. This helped increase in catalytic performance, prevention of agglomerated particle catalysts at high temperature and coke forming after a long time operation. The CH4 conversion of the PSCs containing CeO2–NiO flowers in the dry reforming of CH4 was much higher (nearly 90%) with a smaller Ni content in comparison with the PSC without the CeO2 flowers (with higher Ni content of 8.6%). Moreover, the PSCs with the flowers exhibited an excellent catalytic stability with the degradation of CH4 conversion of only 3.1% after 50 h of reforming. In addition, the high oxygen storage capacity and oxygen mobility of CeO2 resulted in a partial removal of coke forming on the catalyst particles during reforming. This indicated that the catalytic activity of the Ni particles dispersed on the CeO2 flowers for dry reforming of CH4 was superior to that of various Ni-based catalyst systems which had much higher Ni contents. Therefore, it is possible to use the PSCs containing CeO2–Ni flowers to generate hydrogen for use as fuels from dry reforming of CH4.

Original languageEnglish
Pages (from-to)18363-18375
Number of pages13
JournalInternational Journal of Hydrogen Energy
Issue number36
Publication statusPublished - Jul 17 2020

All Science Journal Classification (ASJC) codes

  • Renewable Energy, Sustainability and the Environment
  • Fuel Technology
  • Condensed Matter Physics
  • Energy Engineering and Power Technology


Dive into the research topics of 'Paper-structured catalyst containing CeO2–Ni flowers for dry reforming of methane'. Together they form a unique fingerprint.

Cite this