Overview of the US-Japan collaborative investigation on hydrogen isotope retention in neutron-irradiated and ion-damaged tungsten

Masashi Shimada, Y. Hatano, Y. Oya, T. Oda, M. Hara, G. Cao, M. Kobayashi, M. Sokolov, H. Watanabe, B. Tyburska-Püschel, Y. Ueda, P. Calderoni, K. Okuno

Research output: Contribution to journalArticlepeer-review

43 Citations (Scopus)


The effect of neutron-irradiation damage has been mainly simulated using high-energy ion bombardment. A recent MIT report (PSFC/RR-10-4, An assessment of the current data affecting tritium retention and its use to project towards T retention in ITER, Lipschultz et al., 2010) summarizes the observations from high-energy ion bombardment studies and illustrates the saturation trend in deuterium concentration due to damage from ion irradiation in tungsten and molybdenum above 1 displacement per atom (dpa). While this prior database of results is quite valuable for understanding the behavior of hydrogen isotopes in plasma facing components (PFCs), it does not encompass the full range of effects that must be considered in a practical fusion environment due to short penetration depth, damage gradient, high damage rate, and high primary knock-on atom (PKA) energy spectrum of the ion bombardment. In addition, neutrons change the elemental composition via transmutations, and create a high radiation environment inside PFCs, which influences the behavior of hydrogen isotope in PFCs, suggesting the utilization of fission reactors is necessary for neutron-irradiation. Under the framework of the US-Japan TITAN program, tungsten samples (99.99 at.% purity from A.L.M.T. Co.) were irradiated by fission neutrons in the High Flux Isotope Reactor (HFIR), Oak Ridge National Laboratory (ORNL), at 50 and 300 °C to 0.025, 0.3, and 2.4 dpa, and the investigation of deuterium retention in neutron-irradiated tungsten was performed in the Tritium Plasma Experiment (TPE), the unique high-flux linear plasma facility that can handle tritium, beryllium and activated materials. This paper reports the recent results from the comparison of ion-damaged tungsten via various ion species (2.8 MeV Fe2+, 20 MeV W2+, and 700 keV H -) with that from neutron-irradiated tungsten to identify the similarities and differences among them.

Original languageEnglish
Pages (from-to)1166-1170
Number of pages5
JournalFusion Engineering and Design
Issue number7-8
Publication statusPublished - Aug 2012

All Science Journal Classification (ASJC) codes

  • Civil and Structural Engineering
  • Nuclear Energy and Engineering
  • General Materials Science
  • Mechanical Engineering


Dive into the research topics of 'Overview of the US-Japan collaborative investigation on hydrogen isotope retention in neutron-irradiated and ion-damaged tungsten'. Together they form a unique fingerprint.

Cite this