Magnetic properties of ion irradiated epitaxial Fe films

Y. Kamada, H. Watanabe, S. Mitani, J. Echigoya, J. N. Mohapatra, H. Kikuchi, S. Kobayashi, K. Takanashi

Research output: Contribution to journalArticlepeer-review

8 Citations (Scopus)


Magnetic properties of a heavy-ion irradiated single crystalline iron film were investigated. A high quality Fe (001) film with a thickness of 250 nm was fabricated on MgO (001) using the molecular beam epitaxy technique. The film was irradiated by 3.2 MeV Ni ions at room temperature using a tandem accelerator. Formation of dislocation loops with nanometer size was observed by TEM observation, and that of sub-nanometer size vacancy clusters was confirmed indirectly from a resistivity increase. However, M-H hysteresis curves and magnetic domain structure did not change significantly. These results indicate the formation of irradiation defects of pure iron in nanometer scale range has little influence on the magnetization process of the iron.

Original languageEnglish
Article number012035
JournalJournal of Physics: Conference Series
Issue number1
Publication statusPublished - 2011

All Science Journal Classification (ASJC) codes

  • General Physics and Astronomy


Dive into the research topics of 'Magnetic properties of ion irradiated epitaxial Fe films'. Together they form a unique fingerprint.

Cite this