Lattice defects introduced into LaNi5-based alloys during hydrogen absorption/desorption cycling

Junko Matsuda, Yumiko Nakamura, Etsuo Akiba

Research output: Contribution to journalArticlepeer-review

29 Citations (Scopus)


LaNi5-based intermetallic compounds before and after hydrogen absorption/desorption cycling were observed by transmission electron microscopy. Both a-type and c-type dislocations, which had respective Burgers vectors of 1/3<112̄0> and <0 0 0 1> in the 011̄0 slip plane, were introduced into LaNi5, LaNi4.5Cu0.5 and LaNi4.5Fe0.5 after the first absorption/desorption cycle. These alloys exhibited large difference in the equilibrium pressure between the first absorption and first desorption. Dislocations were introduced during hydrogenation in order to accommodate lattice mismatch between the metal-hydrogen solid solution and the metal hydride; furthermore, the interface between the solid solution and hydride was suggested to be the 011̄0 plane. In contrast, neither dislocations nor stacking faults were observed in LaNi4.5Si0.5, LaNi4.5Al0.5 and LaNi4.75Sn0.75, which showed little or no hysteresis in the hydrogen pressure-composition isotherms. Excess pressure was needed in the absorption process for the formation of misfit dislocations.

Original languageEnglish
Pages (from-to)7498-7503
Number of pages6
JournalJournal of Alloys and Compounds
Issue number27
Publication statusPublished - Jul 7 2011

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry


Dive into the research topics of 'Lattice defects introduced into LaNi5-based alloys during hydrogen absorption/desorption cycling'. Together they form a unique fingerprint.

Cite this