Large single-crystal Ge-on-insulator by thermally-assisted (~400 °C) Si-seeded-pulse-laser annealing

T. Sadoh, M. Kurosawa, A. Heya, N. Matsuo, M. Miyao

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)


Low temperature (≤400 °C) formation of orientation-controlled large (≥10 µm) Ge-on-insulator (GOI) structures is desired to fabricate 3-dimensional large-scale integrated circuits (LSIs), where Ge-based functional devices are stacked on Si-LSIs. For this purpose, Si-seeded pulse-laser annealing (PLA) combined with low-temperature substrate heating (≤400 °C) has been developed. Here, a-Ge stripes on Si substrates partially covered with insulating films are subjected to PLA, where single edges of the a-Ge stripes directly contact Si-seeding substrates through opening windows of insulating films. PLA at room temperature generates lateral growth of Ge layers from Si-seeding substrates. However, the growth length is short (~1 µm), which is attributed to very short melting time. To increase the melting time, low-temperature (≤400 °C) substrate heating during PLA is examined. As a result, very large (~20 µm) orientation-controlled GOI is obtained by combining substrate heating (400 °C) with PLA. Detailed electron microscopy analysis reveals very high crystallinity of the grown layers. Consequently, high-quality rapid-melting growth of Ge becomes possible at a low processing temperature of ~400 °C. This thermally-assisted (~400 °C) Si-seeded PLA will facilitate realization of 3-dimensional LSIs.

Original languageEnglish
Pages (from-to)8-11
Number of pages4
JournalMaterials Science in Semiconductor Processing
Publication statusPublished - Nov 1 2017

All Science Journal Classification (ASJC) codes

  • General Materials Science
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering


Dive into the research topics of 'Large single-crystal Ge-on-insulator by thermally-assisted (~400 °C) Si-seeded-pulse-laser annealing'. Together they form a unique fingerprint.

Cite this