Influence of the addition of silsesquioxane on the dewetting behavior of polystyrene thin film

Nao Hosaka, Keiji Tanaka, Hideyuki Otsuka, Atsushi Takahara

Research output: Contribution to journalArticlepeer-review

20 Citations (Scopus)


A strategy to suppress the dewetting of polystyrene (PS) thin films by the addition of octacyclopentylsilsesquioxane (cPOSS) as a nanofiller was proposed. PS thin films with cPOSS were prepared by spin-coating. The bulk glass transition temperature of PS was not changed with an addition of the nanofiller up to 10 wt%. On the other hand, the addition of cPOSS to the PS thin films led to a great inhibition of dewetting. After annealing for 3 h at 373 K, no appreciable dewetting was observed by optical microscopy in the PS film with 15 wt% cPOSS, in contrast, the PS film without cPOSS was completely dewetted. Holes formed on the PS films with 10 wt% cPOSS. However, in that case, the growth of the holes stopped before reaching the final stage of the dewetting. This suggests that the increase of the cPOSS concentration per unit area at the rim of the holes prevents further growth of the holes, and this inhibition effect can be attributed to the interaction between cPOSS and the substrate accompanying modification of the PS-substrate interface.

Original languageEnglish
Pages (from-to)297-306
Number of pages10
JournalComposite Interfaces
Issue number4
Publication statusPublished - 2004

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • General Physics and Astronomy
  • Surfaces, Coatings and Films


Dive into the research topics of 'Influence of the addition of silsesquioxane on the dewetting behavior of polystyrene thin film'. Together they form a unique fingerprint.

Cite this