Influence of size and proximity of paint coating defects on corrosion behavior of carbon steel plates

Shigenobu Kainuma, Junji Kobayashi, Kazuhiro Utsunomiya, Tatsuro Sakamoto

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)


For paint-coated steel structures, corrosion tends to propagate not only from individual coating defects but also from a plurality of adjacent coating defects that, by interacting with each other, accelerates the corrosion process. However, the influence of size and proximity of the coating defect on corrosion behavior is ambiguous and unclear. In this research, combined cyclic corrosion tests were conducted over a prolonged period using paint-coated steel plates with single and two adjacent circular defects. The test results indicate that the mean and maximum corrosion depths increased when a single defect of the coated steel plate was larger. The corrosion growth rate for specimens with two adjacent circular defects was greater than the one with a single defect. Furthermore, in order to clarify the electrochemical mechanism between two adjacent circular defects, time-dependent corrosion current was measured using a model specimen with these defects.

Original languageEnglish
Pages (from-to)84-97
Number of pages14
JournalJournal of Japan Society of Civil Engineers
Issue number1
Publication statusPublished - 2020

All Science Journal Classification (ASJC) codes

  • Environmental Engineering
  • Civil and Structural Engineering


Dive into the research topics of 'Influence of size and proximity of paint coating defects on corrosion behavior of carbon steel plates'. Together they form a unique fingerprint.

Cite this