Improving the Si impurity tolerance of Pr0.1Ce0.9O2-δ SOFC electrodes with reactive surface additives

Liang Zhao, Nicola H. Perry, Takeshi Daio, Kazunari Sasaki, Sean R. Bishop

Research output: Contribution to journalArticlepeer-review

35 Citations (Scopus)


Fast oxygen exchange kinetics, a key figure of merit in solid oxide fuel cell (SOFC) electrodes, is often dramatically hindered by the presence of even small concentrations of impurities, for example, Si which is common in ceramics processing. In this work, rapid degradation of oxygen exchange kinetics was found on dense thin films of Pr0.1Ce0.9O2-δ (PCO), a mixed ionic electronic conducting electrode for SOFCs, using a new optical transmission relaxation (OTR) technique which facilitates kinetics measurements of bare film surfaces (i.e., in the absence of current collectors typical of conventional measurements). Si was identified by TEM and XPS as a significant impurity, forming a blocking layer on the electrode surface. Full recovery of oxygen exchange kinetics on the measured samples was achieved after deposition of a La oxide film. Subsequent TEM studies indicate the formation of a porous La- and Si-containing film. Interaction between La and Si oxides was identified by a shift in the O 1s XPS peak and a systematic OTR study of films that likely react with Si (e.g., La, Sm oxides) and those that do not (e.g., Nb, Ti, Zn oxides). Preliminary measurements of OTR on a La-PCO solid solution indicates improved long-term electrode kinetics stability, demonstrating the commercial potential of this method to achieve Si impurity tolerance.

Original languageEnglish
Pages (from-to)3065-3070
Number of pages6
JournalChemistry of Materials
Issue number8
Publication statusPublished - Apr 28 2015

All Science Journal Classification (ASJC) codes

  • General Chemistry
  • General Chemical Engineering
  • Materials Chemistry


Dive into the research topics of 'Improving the Si impurity tolerance of Pr0.1Ce0.9O2-δ SOFC electrodes with reactive surface additives'. Together they form a unique fingerprint.

Cite this