Hydrogen-modified dislocation structures in a cyclically deformed ferritic-pearlitic low carbon steel

Shuai Wang, Akihide Nagao, Petros Sofronis, Ian M. Robertson

    Research output: Contribution to journalArticlepeer-review

    45 Citations (Scopus)


    The fatigue-crack growth rate of a ferritic-pearlitic low carbon steel was faster when the tests were conducted in high-pressure H2 gas environments than in air. The predominant fracture feature changed from ductile fatigue striations with some “quasi-cleavage-like” regions when the test was conducted in air to mixed “quasi-cleavage” and “flat” facets when tested in a H2 gas environment. The microstructure beneath the fracture surfaces produced in air was sub-grains, and over a distance of 15 μm from the fracture surface, the dimensions of the sub-grains increased. With hydrogen, dense dislocation bands and refined dislocation cells existed beneath the “quasi-cleavage” and “flat” fracture surfaces. The cell size increased with distance from the fracture surface. The decrease in the dimensions of the key microstructural features as the fracture surface is approached is attributed to the propagation of the crack through an already deformed matrix. The differences in evolved dislocation structure are explained in terms of the hydrogen-enhanced localized plasticity mechanism, and the hydrogen-modified dislocation structure establishes the local conditions that promote the fracture mode transition from ductile fatigue striations to a mixture of “quasi-cleavage” and “flat” features, which directly leads to enhanced fatigue-crack growth.

    Original languageEnglish
    Pages (from-to)164-176
    Number of pages13
    JournalActa Materialia
    Publication statusPublished - Feb 1 2018

    All Science Journal Classification (ASJC) codes

    • Electronic, Optical and Magnetic Materials
    • Ceramics and Composites
    • Polymers and Plastics
    • Metals and Alloys


    Dive into the research topics of 'Hydrogen-modified dislocation structures in a cyclically deformed ferritic-pearlitic low carbon steel'. Together they form a unique fingerprint.

    Cite this