Growth of square Si single bulk crystals with large side-face widths using noncontact crucible method

The noncontact crucible method was used to prepare square Si single bulk crystals. The size of the square part of the ingots was determined by the side-face width of the four-cornered pattern that appeared on the top surface. We obtained square Si single crystals with sizes of 9.4 ' 9.7 and 10.9 ' 11.0cm2 that had no fan-shaped {110} faces and had diagonal lengths of up to 91% of the crucible diameter. To obtain large square Si single bulk crystals with a large side-face width using the present method, the importance of establishing a larger low-temperature region in the Si melt while maintaining a smaller initial temperature reduction was considered.