Giant magnetic entropy change in hydrogenated La(Fe0.88Si0.12)13Hy compounds

Asaya Fujita, Shun Fujieda, Kazuaki Fukamichi, Yoshihiro Yamazaki, Yoshiaki Iijima

Research output: Contribution to journalArticlepeer-review

58 Citations (Scopus)


A magnetic entropy change ΔSM due to the itinerant-electron metamagnetic (IEM) transition was estimated to be -23 J/kg K around the Curie temperature for La(Fe0.88Si0.12)13 in the magnetic field change from 0 to 5 T. In order to control the Curie temperature while keeping such a large value of ΔSM, hydrogen absorption was carried out. La(Fe0.88Si0.12)13H1.0 with TC = 274 K shows a large ΔSM due to the IEM transition around room temperature. The adiabatic temperature change ΔTad from 0 to 2 T is about 7 K, comparable to that of Gd5(Ge0.5Si0.5)4. By changing the hydrogen concentration, the Curie temperature can be controlled from 195 to 336 K. It should be noted that the magnitude of ΔSM is almost the same after hydrogen absorption. Therefore, the hydrogenated La(Fe0.88Si0.12)13Hy compounds are promising magnetic refrigerants working in a wide range of temperature.

Original languageEnglish
Pages (from-to)1202-1204
Number of pages3
JournalMaterials Transactions
Issue number5
Publication statusPublished - May 2002
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • General Materials Science
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering


Dive into the research topics of 'Giant magnetic entropy change in hydrogenated La(Fe0.88Si0.12)13Hy compounds'. Together they form a unique fingerprint.

Cite this