Formation mechanism of bainitic ferrite in an Fe-2 Pct Si-0.6 Pct C alloy

Kaneaki Tsuzaki, Aki Kodai, Tactashi Maki

Research output: Contribution to journalArticlepeer-review

46 Citations (Scopus)


The bainite transformation at 723 K in an Fe-2 pct Si-0.6 pct C alloy (mass pct) was investigated with transmission electron microscopy (TEM) and quantitative metallography to clarify the growth mechanism of the ferritic component of bainite. In early stages of transformation, the bainitic ferrite was carbide free. The laths of bainitic ferrite within a packet were parallel to one another and separated by carbon-enriched retained austenite. The average carbon concentration of the bainitic ferrite was estimated to be 0.19 mass pct at the lowest, indicating that the ferrite was highly supersaturated with respect to carbon. The laths did not thicken during the subsequent isothermal holding, although they were in contact with austenite of which the average carbon concentration was lower than the paraequilibrium value. In the later stage of transformation, large carbide plates formed in the austenite between the laths, resulting in the decrease in the carbon concentration of the austenite. Subsequently, the ferrite with a variant different from the initially formed ferrite in the packet was decomposed for the completion of transformation. The present results indicate that the bainitic ferrite develops by a displacive mechanism rather than a diffusional mechanism.

Original languageEnglish
Pages (from-to)2009-2016
Number of pages8
JournalMetallurgical and Materials Transactions A
Issue number9
Publication statusPublished - Sept 1994
Externally publishedYes

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys


Dive into the research topics of 'Formation mechanism of bainitic ferrite in an Fe-2 Pct Si-0.6 Pct C alloy'. Together they form a unique fingerprint.

Cite this