Electrochemical and thermal properties of hard carbon-type anodes for Na-ion batteries

Jie Zhao, Liwei Zhao, Kuniko Chihara, Shigeto Okada, Jun Ichi Yamaki, Shingo Matsumoto, Satoru Kuze, Kenji Nakane

Research output: Contribution to journalArticlepeer-review

144 Citations (Scopus)


The hard carbon C1600 was studied as an anode material for Na-ion batteries. The electrochemical performance of the C1600 electrode was investigated in four kinds of typical electrolytes: 1 mol dm-3 NaClO4/EC-DMC, 1 mol dm-3 NaClO4/PC, 1 mol dm-3 NaPF6/EC-DMC, and 1 mol dm-3 NaPF6/PC. The C1600 electrodes showed excellent electrochemical properties in NaClO4-containing electrolytes. An initial Na insertion/extraction capacity of 413/321 mAh g-1 was obtained in the NaClO4/EC-DMC electrolyte, followed by a good capacity retention of 90% over 50 cycles. These are the best electrochemical properties reported thus far for carbonaceous anode materials in Na-ion batteries. The safety risk of C1600 anodes for Na-ion batteries was evaluated by using a TG-DSC system. Based on the results of DSC analysis for simple electrolytes, the thermal behaviors of mixtures of the sodiated/lithiated C1600 and the associated electrolyte in a temperature range from room temperature to 400 °C were investigated and compared. The C1600 anodes showed better thermal stability in EC-DMC-based electrolytes than in PC-based ones. Moreover, although Na metal is much more unstable than Li metal, the anode and electrolyte mixture of Na-ion batteries showed similar or better thermal stability than that of Li-ion batteries.

Original languageEnglish
Pages (from-to)752-757
Number of pages6
JournalJournal of Power Sources
Publication statusPublished - 2013

All Science Journal Classification (ASJC) codes

  • Renewable Energy, Sustainability and the Environment
  • Energy Engineering and Power Technology
  • Physical and Theoretical Chemistry
  • Electrical and Electronic Engineering


Dive into the research topics of 'Electrochemical and thermal properties of hard carbon-type anodes for Na-ion batteries'. Together they form a unique fingerprint.

Cite this