3 at. % nitrogen-doped ultrananocrystalline diamond/hydrogenated amorphous carbon composite (UNCD/a-C:H) films were synthesized by coaxial arc plasma deposition. Optically, the films possess large absorption coefficients of more than 105 cm-1 at photon energies from 3 to 5 eV. The optical band gap was estimated to be 1.28 eV. This value is smaller than that of undoped films, which might be attributable to increased sp2 fractions. The temperature dependence of the electrical conductivity implies that carrier transport follows a hopping conduction model. Heterojunctions with p-type Si substrates exhibited a typical rectifying action. From the capacitance-voltage characteristics that evidently indicated the expansion of a depletion region into the film side, the built-in potential and carrier concentration were estimated to be 0.51 eV and 7.5 × 1016 cm-3, respectively. It was experimentally demonstrated that nitrogen-doped UNCD/a-C:H films are applicable as an n-type semiconductor.
All Science Journal Classification (ASJC) codes
- General Engineering
- General Physics and Astronomy