Effect of palladium addition on the tarnishing of dental gold alloys

M. Ohta, M. Nakagawa, S. Matsuya

Research output: Contribution to journalArticlepeer-review

10 Citations (Scopus)


Tarnishing tests were carried out on Au-Cu-Ag and Au-Cu-Pd alloys. This study focused on the individual and combined effects of nobility, palladium content and microstructure. Tarnish resistance was almost perfect for the alloys with nobility higher than 50 at%, but it seemed to relate to the palladium : gold atomic ratio for the alloys with low nobility. Palladium inclusion reduced the tarnish susceptibility up to about 10 at%. This decrease in the degree of tarnishing was attributed to the decrease in the diffusion rate of S2 ion which resulted in a decrease in the growth rate of sulphide layer. Tarnishing of the alloy with low nobility was very sensitive to its microstructure. The tarnishing susceptibility of dual-phase Au-Cu-Ag alloy was twice as high as that of the single-phase alloy. However, palladium-bearing alloy showed no increase in the degree of tarnishing by phase separation. This may be attributed to the enrichment of palladium in the copper-rich phase.

Original languageEnglish
Pages (from-to)140-145
Number of pages6
JournalJournal of Materials Science: Materials in Medicine
Issue number3
Publication statusPublished - Oct 1990

All Science Journal Classification (ASJC) codes

  • Biophysics
  • Bioengineering
  • Biomaterials
  • Biomedical Engineering


Dive into the research topics of 'Effect of palladium addition on the tarnishing of dental gold alloys'. Together they form a unique fingerprint.

Cite this